Repository logo
 

Faculty of Engineering and Built Environment

Permanent URI for this communityhttp://ir-dev.dut.ac.za/handle/10321/9

Browse

Author: search.filters.author.Singh, Shalini

Search Results

Now showing 1 - 2 of 2
  • Thumbnail Image
    Item
    A study of the chemical quality of ambient air at selected intersections in the Durban Metropolis
    (2003) Singh, Shalini; Moodley, K. G.
    Motor vehicles are considered a major source of air pollution in urban environments. Nitrogen dioxide (N02) and nitric oxide (NO) which are collectively referred to as oxides of nitrogen (NOx) are formed at high temperatures during combustion processes in the engines of motor vehicles and are emitted via the exhaust into the atmosphere. Nitrogen dioxide is regarded as an irritant of the respiratory system.
  • No Thumbnail Available
    Item
    Bulk cure study of nanoclay filled epoxy glass fiber reinforced composite material
    (De Guyter, 2016) Olusanya, John; Kanny, Krishnan; Singh, Shalini
    The correlation between cure properties and structure of nanoclay filled composite laminate has not been studied extensively. Most of the cure studies were preferably done using small samples through a calorimetric method. In this study, the effect of varying weight ratio of nanoclay (1–5 wt%) on bulk cure properties of epoxy glass fiber reinforced composite (GFRC) laminates was studied. Bulk cure of unfilled and clay filled GFRC laminates was determined using the dynamic mechanical analysis-reheat method (DMA-RM). DMA-RM cure properties gave a better coordinate method, with better cure efficiency achieved in clay filled GFRC laminates when compared to unfilled GFRC laminates. The correlation between nanoclay and DMA-RM degree of cure was coordinated with compressive and in-plane shear strength properties. The degree of cure value of 78% by DMA-RM at 1 wt% clay filled GFRC corresponds with the compressive modulus and in-plane shear strength highest values, which are 20% and 14% increase, respectively, also at 1 wt% clay filled GFRC. The structures of the unfilled and clay filled epoxy were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Clay filled epoxy up to 3 wt% showed no distinct diffraction peak, which suggested that nanoclay is randomly dispersed in the matrix.